RUIBIO 4001

PHA (Polyhydroxyalkanoates) Resin

MFR(190℃,2.16kg): 3-15 g/10min
HDT(0.455MPa): 120-130 ℃
Flexural Modulus: 1900-2400 MPa

Suitable for injection molding, casting, extrusion, coating, straw, fiber, 3D priting, blistering and other processes. Suitable for blending modification of biodegradable materials.

RUIBIO 4002

PHA (Polyhydroxyalkanoates) Resin

MFR(190℃,2.16kg): 3-15 g/10min
HDT(0.455MPa): ＞130 ℃
Flexural Modulus: 2200-2700 MPa

Suitable for injection molding, casting, extrusion, coating, straw, fiber, 3D priting, blistering and other processes. Suitable for blending modification of biodegradable materials.

RUIBIO 4003

PHA (Polyhydroxyalkanoates) Resin

MFR(190℃,2.16kg): ≤10 g/10min HDT(0.455MPa): 60-70 ℃ Elongation at Break: 100%

Suitable for injection molding, casting, extrusion, coating, straw, fiber, 3D priting, blistering and other processes. Suitable for blending modification of biodegradable materials.

RUIBIO 5010

Bio-PE (Biobased Polyethylene)

MFR(190℃,2.16kg): ≤3 g/10min Biobased Carbon Content: 10-80%

Ideal for stretch film, protective packaging, agricultural film, and various logistics solutions

RUIBIO F6000

Modified PLA Compound

PLA/PBAT Blend, Mineral-filled Density :1.35-1.45 g/cm³ MFR(190℃,2.16kg):2-5 g/10min

Shopping bags Garbage bags Express mailers

RUIBIO F6001

Modified PLA Compound

Mineral powder-filled
Density : 1.30-1.35 g/cm³
MFR(190℃,2.16kg): 6g/10 min

Shopping bags T-shirt bags Produce bags

RUIBIO F6003

Modified PLA Compound

PBAT/PLA Blend, Mineral-filled Density : 1.24-1.28 g/cm³ MFR(190℃,2.16kg): 2-6 g/10min

Produce bags Shopping bags Garbage bags Disposable Gloves

RUIBIO F6004

Modified PLA Compound

PLA/PBAT Blend, Mineral-filled Density : 1.30-1.40 g/cm³ MFR(190℃,2.16kg): 3-6 g/10min

Biodegradable Mulch Film

RUIBIO T6000

Modified PLA Compound

High toughness
Density : 1.34 g/cm³
MFR(190℃,2.16kg): 11 g/10min

Bendable straws

RUIBIO T6001

Modified PLA Compound

High stiffness
Density : 1.36 g/cm³
MFR(190℃,2.16kg): 3.8 g/10min

Straight straws